Anaerobically-curing compositions

ABSTRACT

Anaerobically-curing compositions are described comprising (A) a polymerizable monomer; (B) a halogen-containing compound as a first initiator component; (C) an amine, organic sulfimide or perfluoroalkyl sulfonanilide as a second initiator component; and (D) an inhibitor of free-radical polymerization. These compositions are particularly suitable as adhesives and may be formulated as thread-locking adhesives or may be modified by the addition of various modifying polymers to obtain desired properties such as increased viscosities or pressure-sensitive properties.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation-in-part of copending U.S. applicationSer. No. 203,682 which was filed on Nov. 3, 1980 and now abandoned.

BACKGROUND OF THE INVENTION

This invention relates to anaerobically-curing compositions.

Anaerobically-curing compositions generally comprise polymerizableacrylate monomers and free-radical initiators. When maintained in anoxygen-containing environment, such compositions remain uncured (i.e.,unpolymerized). However, in the absence of oxygen, such as when ananaerobically-curing composition is placed between surfaces which are inclose engagement with one another (e.g. a nut and bolt), cure willensue.

Anaerobically-curing compositions containing peroxide or hydroperoxideinitiators are well-known in the art, having been described in U.S. Pat.No. 2,895,950 (Krieble). Commonly such compositions contain quinonetypecompounds which act as polymerization inhibitors, thereby maintainingthe compositions in an uncured state when stored in the presence ofoxygen.

Unfortunately, anaerobically-curing compositions which contain peroxideor hydroperoxide initiators may possess certain disadvantages. Forexample, there is often the possibility of explosion whenever largeamounts of peroxy compounds are handled such as during manufacture ofthese compositions. Furthermore, unfortunately peroxy compoundstypically decompose with time, thus resulting in a steadily decreasingability of such compounds to initiate the polymerization of compositionscontaining them.

While one-part, anaerobically-curing compositions containingpolymerization initiators other than peroxy compounds are known in theart, such compositions often fail to exhibit a suitable balance ofshelf-life stability versus cure-rate. In particular, while suchcompositions may exhibit suitable shelf-life stability in the presenceof oxygen, they may cure at unsatisfactory rates when oxygen isexcluded. Alternatively, such compositions may often cure rapidly in theabsence of oxygen, but may exhibit unsatisfactory shelf-lives.

BRIEF SUMMARY OF THE PRESENT INVENTION

The present invention provides novel anaerobically-curing compositionscomprising (A) a polymerizable monomer having at least oneα,β-unsaturated carboxyl functionality per molecule of monomer; (B) ahalogen-containing compound as a first initiator component; (C) as asecond initiator component a compound selected from the group consistingof amines, organic sulfimides, and perfluoroalkyl sulfonanilides; and(D) an inhibitor of free-radical polymerization.

The compositions of the present invention exhibit suitable shelf-life(e.g., at least about 4 weeks at 120° F.) when stored in the presence ofoxygen and cure rapidly to form strong bonds in the absence of oxygen.Furthermore, the compositions of the present invention, since they donot contain peroxides or hydroperoxides, may be stored for extendedperiods of time without fear of initiator decomposition. Also, since thecompositions of the present invention do not contain peroxides orhydroperoxides, there is no possibility of explosion duringmanufacturing of these compositions.

The compositions of the present invention are particularly suitable forbonding operations involving at least one active metal (e.g., copper andcold-rolled steel) and are further suitable for bonding relativelyinactive metals (e.g., zinc and cadmium). The compositions are alsosuitable for bonding nonmetallic substrates (e.g., plastic, glass andwood) provided that appropriate primers are used to accelerate the cureto a useful rate.

The compositions of the present invention may be formulated asnon-viscous, flowable liquids which are particularly useful in bondingoperations involving well-mated surfaces (e.g., a nut and bolt). Thecompositions may also comprise various types of modifying polymers inorder to obtain desired properties. For example, thermoplastic polymersor pressure-sensitive polymers may be added to the compositions of thepresent invention to obtain compositions which are useful in a varietyof other bonding operations.

DETAILED DESCRIPTION OF THE PRESENT INVENTION

The anaerobic compositions of the present invention comprise 100 partsby weight of a polymerizable monomer (A) having at least oneα,β-unsaturated carboxyl functionality (i.e., ##STR1## per molecule ofmonomer. Suitable monomers for employment in the compositions of thepresent invention include the diacrylates and dimethacrylates describedin U.S. Pat. No. 3,043,820 (Krieble), U.S. Pat. No. 3,457,212 (Fukuokaet al.), U.S. Pat. No. 3,923,737 (George et al.), and U.S. Pat. No.3,944,521 (Bradley et al.), incorporated herein by reference. Othersuitable polymerizable monomers include acrylate-terminated monomerssuch as the monomeric polyacrylate esters formed from organicpolyisocyanates, such monomers being described, for example, in U.S.Pat. No. 3,425,988 (Gorman et al.), incorporated herein by reference.Particularly suitable polyfunctional acrylates and methacrylates includetriethyleneglycol dimethacrylate, ethyleneglycol dimethacrylate,tetraethyleneglycol dimethacrylate, polyethyleneglycol, diacrylate,polyethyleneglycol dimethacrylate, 1,3-butyleneglycol dimethacrylate,trimethylol propane trimethacrylate, neopentylglycol dimethacrylate,ethoxylated bisphenol A dimethacrylate, propoxylated bisphenol Cdimethacrylate and bisphenol A bis(2-hydroxypropyl)dimethacrylate.

Monoacrylates and monomethacrylates are also suitable for employment inthe compositions of the present invention as the polymerizable monomer.Suitable monoacrylates and monomethacrylates include cyclohexylmethacrylate, 2-ethylhexyl methacrylate, hydroxyethyl methacrylate,isooctyl acrylates and n-butyl acrylate.

Methacrylic acid and similar α,β-unsaturated carboxylic acids are alsosuitable for employment as polymerizable monomers in the compositions ofthe present invention as are half-ester such as the 2-hydroxyethylmethacrylate half-ester of maleic acid. Other suitable half-estersinclude those described in U.S. Pat. No. 3,428,614 (Brownstein) and U.S.Pat. No. 4,080,238 (Wolinski et al.), incorporated herein by reference.

In order to enhance the shelf-life of the compositions of the presentinvention it may be desirable to remove metal ions, if such are present,from the polymerizable monomer. This may be particularly desirable inthe event that commercially-obtained monomers, which often containsignificant amounts of metal ions, are employed in these compositions.Removal of metal ions may be effected by means known to those skilled inthe art.

The compositions of the present invention may comprise a single type ofpolymerizable monomer or may comprise a blend of two or more differentpolymerizable monomers.

Compositions of the present invention further comprise about 0.5 to 20parts by weight and preferably 1 to 10 parts by weight of ahalogen-containing compound (B) as a first initiator component per 100parts by weight of the polymerizable monomer (A). Generally thehalogen-containing compound should be of an electronic structure whichfacilitates free-radical formation. One such class of suitablehalogen-containing compounds is defined by the following general formula(I): ##STR2## wherein:

X¹ is selected from the group consisting of H, CH₃, Cl, and Br;

Y¹ and Z¹ are each selected independently from the group consisting ofCl and Br;

R¹ is selected from the group consisting of aromatic and heteroaromaticresidues; and n is an integer from 1 to 3 inclusive.

It is to be understood that the formula (I) may contain any substituentwhich does not adversely affect the compound for its intended use as aninitiator component.

Examples of suitable halogen-containing compounds of the above formula(I) are α,α,α-trichlorotoluene, α,α,α,α',α',α'-hexachloro-p-xylene,α,α,α-tribromoquinaldine, ##STR3##

Preferred halogen-containing compounds of the above general formula (I)are further defined by the following formula (II): ##STR4## wherein:

X³ and X⁴ are each selected independently from the group consisting ofH, CH₃, Cl, and Br;

Y³, Y⁴, Z³ and Z⁴ are each independently selected from the groupconsisting of Cl and Br; and

R³ is selected from the group consisting of H and organic radicalscomprising 1 to about 10 carbons. Preferred organic radicals are alkyl,haloalkyl, alkylene and aromatic groups.

It is to be understood that R³ of formula (II) may contain anysubstituent which does not adversely affect the compound for itsintended use as an initiator component.

Suitable halogen-containing compounds of formula (II) include thosedescribed in U.S. Pat. No. 3,277,091 (Schmelzer et al.) and U.S. Pat.Nos. 3,954,475 and 3,987,037 (both to Bonham et al.), incorporatedherein by reference. Examples of this preferred class are2,4-Bis-(trichloromethyl)-6-methyl-s-triazine,2,4,6-Tris-(trichloromethyl)-s-triazine,2,4,6-Tris-(tribromomethyl)-s-triazine, and2,4-Bis(trichloromethyl)-6-p-methoxystryryl-s-triazine, all prepared inaccordance with the teachings of Wakabayashi et al., Bulletin of theChemical Society of Japan, 42, 2924-30 (1969), an article referenced insaid U.S. Pat. Nos. 3,954,475 and 3,987,037, and ##STR5## prepared inaccordance with the teachings of said U.S. Pat. No. 3,277,091.

A second class of suitable halogen-containing compounds is defined bythe following general formula (III): ##STR6## wherein:

X² is selected from the group consisting of H, Cl, Br and CN;

Y² and Z² are each selected independently from the group consisting ofCl and Br;

R² is selected from the group consisting of amino residues and organicradicals, preferably hydrocarbons, comprising 1 to about 10 carbons.Preferred hydrocarbon groups are alkyl groups and aryl groups;

p is 0 or 1;

q is 0 or 1; and

r is 1 or 2.

It is to be understood that R² of the formula (III) may contain anysubstituent which does not adversely affect the compound for itsintended use as an initiator component.

Examples of suitable halogen-containing compounds of this generalformula (III) are dibromocyanoacetamide, CH₃ CH₂ CH(CH₂ CO₂ CBr₃)₂, CH₃CH₂ CH(CH₂ CO₂ CBr₃)₂, ##STR7##

The compositions of the present invention may comprise a single type ofhalogen-containing compound or may comprise two or more different typesof halogen-containing compounds.

Compositions of the present invention also comprise as a secondinitiator component (C) a compound selected from the group consisting ofamines, organic sulfimides, and perfluoroalkyl sulfonanilides. Thecompositions of the present invention comprise about 0.5 to 20 parts byweight and preferably 1 to 10 parts by weight of the second initiatorcomponent per 100 parts by weight of the polymerizable monomer.Furthermore, it is preferred that the second initiator component bepresent in these compositions in amounts which are approximatelystoichiometric to the halogen-containing compound (B).

Amines useful in the compositions of the present invention are secondaryamines and tertiary amines. Suitable secondary amines are of thefollowing formula (IV): ##STR8## wherein: R⁴ and R⁵ are each organicradicals, preferably hydrocarbon groups, comprising 1 to about 12carbons. It is to be understood that R⁴ and R⁵ of formula (IV) can beunited to form a heterocyclic secondary amine.

Examples of suitable secondary amines of formula (IV) areN,N-diethylamine, N,N-diphenylamine and homopiperidene.

Suitable tertiary amines are of the following formula (V): ##STR9##wherein: R⁶, R⁷ and R⁸ are each organic radicals, preferably hydrocarbongroups, comprising 1 to about 12 carbons. It is to be understood thatany two of R⁶, R⁷ and R⁸ of formula (V) may be combined to form aheterocyclic tertiary amine.

Examples of suitable tertiary amines of the formula (V) are triethylamine, tripropyl amine, tributyl amine, N,N-dimethyl cyclohexyl amine,N,N-dimethyl ethanol amine, and 2-aminopyridine.

Within formula (V) is the preferred class of tertiary amines, namelytertiary aromatic amines of the more specific formula (VI): ##STR10##wherein:

R⁹ and R¹⁰ are each organic radicals, preferably hydrocarbon groups,comprising up to about 12 carbons;

A is a carbocyclic armoatic nucleus selected from the group consistingof phenyl and naphthyl radicals;

R¹¹ is an organic radical comprising up to about 5 carbons and isselected from the group consisting of alkyl and alkoxy radicals; and

t is from 0 to 3 ; inclusive.

Examples of suitable tertiary aromatic amines of formula (VI) areN,N,diethyl-p-toluidine,-N,N-dimethylaniline, N,N-diethylaniline andN,N-bis-(2-hydroxyethyl)-p-toluidine. The preferred tertiary aromaticamine is N,N-dimethyl-p-toluidine.

Organic sulfimides (i.e., organic compounds containing the group##STR11## useful in the compositions of the present invention includethose of the following general formula (VII): ##STR12## wherein: R¹² andR¹³ are organic radicals, preferably hydrocarbon groups, containing upto about 10 carbons. It is to be understood that R¹² and R¹³ of formula(VII) may contain any substituent which does not adversely affect thecompound for its intended use as an initiator component. It is also tobe understood that R¹² and R¹³ of formula VII can be united to bond thesulfimide group in a heterocyclic or a polynuclear heterocyclic ringsystem.

A suitable organic sulfimide of formula (VII) is ##STR13## The preferredorganic sulfimide of formula (VII) is O-benzoic sulfimide (i.e.,saccharin).

Suitable perfluoroalkyl sulfonanilides for employment in thecompositions of the present invention have been described in U.S. Pat.No. 4,005,141 (Moore et al) and U.S. Pat. No. 4,076,519 (Harrington etal), incorporated herein by reference, and includetrifluoromethanesulfonanilide, 2-phenyltrifluoromethanesulfonanilide,and N-2-naphthyltrifluoromethylsulfonanilide, all prepared in a closedractor as described generally in Method A of said U.S. Pat. No.4,005,141, 4-trifluoromethyltrifluoromethanesulfonanilide, prepared asdescribed in said U.S. Pat. No. 4,076,519; and4-phenylthiotrifluoromethanesulfonanilide, prepared as described in saidU.S. Pat. No. 4,005,141. Trifluoromethanesulfonanilide is the preferredperfluoroalkylsulfonanilide for employment in the compositions of thepresent invention.

The compositions of the present invention may comprise one or more typesof amine, organic sulfimide or perfluoroalkylsulfonanilide or variouscombinations thereof.

When an amine is employed as the second initiator component in thecompositions of the present invention, it may also be desirable toinclude up to about 0.5 parts by weight and preferably about 0.1 to 0.3parts by weight of an organic thiol per 100 parts by weight of themonomer. Compositions comprising an amine and an organic thiol aredescribed in copending application Ser. No. 289,702, filed of even dateand commonly assigned, now U.S. Pat. No. 4,413,108, which is acontinuation-in-part of application Ser. No. 203,683, filed on Nov. 3,1980 and commonly assigned, both incorporated herein by reference.

A preferred thiol for employment in N,N-dimethyl-p-toluidine-containingcompositions is dodecyl mercaptan.

In order to obtain compositions exhibiting suitable shelf-life, thecompositions of the present invention also comprise a sufficient amountof an inhibitor of free-radical polymerization to retard polymerizationof the compositions while in the presence of air. Preferred compositionsof the present invention comprise about 0.0005 to 0.10 parts by weightand most preferably about 0.001 to 0.03 parts by weight of conventionalquinone-type inhibitor (i.e., quinone and its derivatives)per 100 partsby weight of the polymerizable monomer (A). Preferred quinone-typeinhibitors for employment in the composition of the present inventionare hydroquinone, methylhydroquinone and benzoquinone. Other suitablequinone-type inhibitors are described in U.S.Pat. No. 4,166,169 (Patelet al.), incorporated herein by reference. Other types of inhibitors offree-radical polymerization which are well-known in the art may also beused in the compositions of the present invention.

Employment of a commercially-obtained polymerizable monomer, whichgenerally will already contain a conventional quinone-type inhibitor(e.g., hydroquinone or methylhydroquinone), may introduce a sufficientamount of the inhibitor into the compositions of the present inventionsuch that it may be unnecessary to separately add additional inhibitor.

Compositions comprising the aforementioned components (A), (B) and (C)generally exhibit low viscosity and are particulary useful for bondingwell mated surfaces such as the threads of a nut and bolt. Fixturing ofthe surfaces involved in the bonding operation may be necessary whenemploying compositions comprising only components (A), (B), and (C)until sufficient bond strength has developed. Fixture time (i.e., thetime required to develop a bond between surfaces which will withstandforces exerted with "hand strength") will typically be within less thanabout 1 hour at room temperture.

In many bonding applications, it may be desirable to achieve bondingcharacteristics not obtainable with compositions comprising onlycomponents (A), (B), and (C). Thus, the compositions of the presentinvention may furthercomprise up to about 950 parts by weight of variousmodifying polymers per 100 parts by weight of the polymerizable monomer(A). Modifying polymers which may be present in these compositionsinclude polymers added to obtain desired viscosities. Other modifyingpolymers which may be present in these compositions includethermoplastic polymers and pressure-sensitive polymers, the latter alsogenerally being thermoplastic in nature. Preferred modifying polymersare substantially nonreactive (i.e., will not generally be subject tofree-radical-initiated polymerizatin under the anaerobic conditionstypically used to cure the compositions of the present invention).

Polymers useful as modifying polymers for providing compositionsexhibiting increased viscosity are well-known in the art and includecellulose acetate butyrates, polymethacrylates, phenoxy resins,polyesters and polyurethanes. A preferred modifying polymer forincreasing viscosities of these compositions is "PKHA Resin" (a phenoxyresin commercially available from Union Carbide). A particularlysuitable amount of the modifying polymers for providing compositionsexhibiting increased viscosities is up to about 25 parts by weight per100 parts by weight of the polymerizable monomer (A).

Thermoplastic polymers useful as modifying polymers in thesecompositions are well-known in the art and include those described inU.S. Pat. No. 3,996,308 (Douek et al.), incorporated herein byreference. Examples of particularly suitable thermoplastic polymersinclude polyvinyl acetates (e.g. that available under the tradedesignation "AYAT Resin" from Union Carbide), phenoxy resins (e.g., thatavailable under the trade designation "PKHJ Resin" from Union Carbide),polyesters (e.g. that available under the trade designation "Vitel 207"from B.F. Goodrich), polyurethanes (e.g. that available under the tradedesignation "Estane 5712" from B.F. Goodrich), and nitrile rubbers(e.g., that available under the trade designation "Hycar 1072" from B.F. Goodrich).

Pressure-sensitive polymers useful as modifying polymers in thesecompositions include those described in U.S. Pat. No. Re. 24,906(Ulrich) and U.S. Pat. No. 4,113,792 (Pastor et al.), both incorporatedherein by reference. Examples of particularly suitablepressure-sensitive polymers include copolymers of isooctyl acrylate andacrylic acid, copolymers of isobutyl acrylate and acrylic acid andcopolymers of n-butyl acrylate and acrylic acid, these copolymerspreferably containing about 90% by weight of the respective alkylacrylate and about 10% by weight of acrylic acid. Another suitablepolymer is the terpolymer containing isobutyl acrylate, n-butyl acrylateand acrylic acid residues.

A particularly suitable amount of thermoplastic or pressure-sensitivemodifying polymers for employment in the compositions of the presentinvention is from about 25 to 500 parts by weight per 100 parts byweight of the polymerizable monomer (A).

Compositions of the present invention which comprise the variousmodifying polymers discussed above may further comprise the varioustackifiers, plasticizers and the like which are well known in the art inorder to obtain desired properties.

Compositions comprising modifying polymers may be conveniently appliedto surfaces as viscous neat liquids, sheets, films, tapes and the like,or as solutions in suitable organic solvents. Depending on the type ofmodifying polymer employed in the composition, fixturing of the surfacesinvolved in the bonding operation may or may not be necessary.

It is understood that the compositions of the present invention may alsocomprise various other ingredients such as fillers, thickening agents,and the like which are well-known in the art.

It is also understood that the compositions of the present invention maybe formulated as two-part compositions with at least one part comprisingas a major constituent a polymerizable monomer and with one partcomprising the first initiator component (i.e., a halogen-containingcompound) and the other part comprising the second initiator component(i.e., an amine, an organic sulfimide or a perfluoroalkylsulfonanilide). If only one part comprises a polymerizable monomer, themonomer-less part may comprise the respective initiator componentcombined with a suitable vehicle such as a volatile organic solvent.Alternatively, if that initiator component is a neat liquid, it can beemployed simply as such.

When the compositions of the present invention are employed in bondingoperations involving at least one active metal surface (e.g., copper andcold-rolled steel), cure will rapidly ensue at room temperature in theabsence of oxygen. However, it is known that anaerobically-curingcompositions, including those of the present invention, may cure onlyvery slowly, if at all, when no active metal surfaces are involved inthe bonding operation. Thus when the compositions of the presentinvention are to be employed in bonding operations involving relativelyinactive metals (e.g., cadmium and zinc) or nonmetal substrates (e.g.,plastic, glass and wood) or combinations thereof, it is often desirableor perhaps even necessary to employ an appropriate activator which ispreapplied to at least one of the surfaces to be bonded. Such anactivator can, of course, be employed to further accelerate cure whenactive metal surfaces are involved in the bonding operation.

Paticularly suitable activators include compounds containing transitionmetal ions, examples of such activators including iron acetylacetonate,vanadium acetylacetonate, and copper octoate. A preferred activator ofthis type is copper acetylacetonate. It may be desirable to employ anactivator having the metal ion in a higher versus lower oxidation state.Other particularly suitable activators are condensation reactionproducts of an aldehyde and a primary or secondary amine, such productsbeing described n U.S. Pat. No. 3,616,040 (Toback), incorporated hereinby reference. A preferred activator of this latter type is acondensation reaction product of butyraldehyde and aniline (e.g., thatcommercially available under the trade designation "Vanax 808" from R.T. Vanderbilt Chemical Company).

The activator may be applied to a substrate by means of a suitablevehicle. For example, the activator may be applied as a solution in avolatile organic solvent. A volatile organic solvent is desirable as avehicle for the activator in order to insure rapid evaporation of thesolvent and to thus reduce the possibility of entrapment of solventbetween the surfaces being bonded as the bonding operation proceeds. Apreferred solvent for use in the present invention is methylenechloride. Activators which are liquids or solids at the temperature atwhich the bonding operatin is conducted may be applied directly to asubstrate without dissolution in a vehicle.

In the following examples which will serve to illustrate the presentinvention all parts are parts by weight and all percentages arepercentages by weight, unless otherwise indicated.

TEST METHODS Accelerated Shelf-life Stability--Test Method A

In testing the accelerated stability of a composition, a 500 ccpolyethylene bottle is filled with approximately 250cc of thecomposition and the bottle is then sealed with a screw cap. The bottleand contents are stored at 120° F. (49° C.) for 28 days, after whichtime the contents are examined for polymerization and for curability.

Overlap Shear--Test Method B

In testing the performance of a composition, 3 to 4 drops (about 0.15 to0.20 cc) of the composition is applied to an etched aluminum strip whichin turn is brought into contact with a second etched aluminum strip suchthat the area of adhesive bonding between the two strips measures1-inch² (6.45 cm²). The etched aluminum strips have previously beenprimed with a 1% solution (w/w) of copper (II) acetylacetonate inmethylene chloride. The handling time (i.e., the time at which the twostrips could no longer be pulled apart with gentle hand pressure) ismeasured in hours. The bond is then allowed to condition for 3 days atroom temperature, at which time overlap shear value (given in pounds persquare inch) is determined using an Instron Dynamic tester with a jawseparation rate of 0.2 inch (0.51 cm) per minute.

Thread Locking--Test Method C

In testing the performance of a composition, one drop (about 0.05 cc) ofthe composition is applied to the threads of a cleaned 3/8 inch (0.95cm) No. 16, grade 5, plain finished steel bolt to which a mating nut issubsequently applied. The fixture time (i.e., the time at which the nutcould no longer be unscrewed from the bolt using hand strength only) isdetermined at room temperture. The nut and bolt assembly is then allowedto condition for 24 hours at room temperature and break away torque andprevailing off torque values are subsequently measured (both given ininch/pounds).

EXAMPLE 1

A suitable anaerobically-curing composition in accordance with thepresent invention is prepared using the following ingredients combinedin the order indicated:

    ______________________________________                                                         Parts by Weight                                              ______________________________________                                        Tetraethyleneglycol dimeth-                                                                      100                                                        acrylate (available under                                                     trade designation "SR-205"                                                    from Sartomer Co.)                                                            2,4-Bis-(trichloromethyl)-6-                                                                     2                                                          methyl-s-triazine (described                                                  in U.S. Pat. No. 3,987,037                                                    (Bonham et al.))                                                              N,N--dimethyl-p-toluidine                                                                        2                                                          Methylhydroquinone 0.01                                                       ______________________________________                                    

When the above composition is tested in accordance with Test Method A,no gelation is observed at 28 days.

When the above composition is tested in accordance with Test Method B,the handling time is less than about 1 hour and the overlap shear valueis about 180 pounds per square inch (12.6 kg/cm²).

EXAMPLE 2

Another suitable one-pat anaerobically-curing composition in accordancewith the present invention is prepared using the following ingredientscombined in the order indicated:

    ______________________________________                                                        Parts by Weight                                               ______________________________________                                        Tetraethyleneglycol                                                                             100                                                         dimethacrylate                                                                2,4-Bis(trichloromethyl)-6-                                                                     3                                                           methyl-2-triazine                                                             o-benzoic sulfimide                                                                             1.6                                                         Methylhydroquinone                                                                              0.05                                                        ______________________________________                                    

When the above composition is tested in accordance with Test Method A,no gelation is observed at 28 days.

When the above composition is tested in accordance with Test Method B,the handling time is less than about 1 hour.

When the above composition is tested in accordance with Test Method C,the fixture time is less than about 1 hour, the breakaway torque isabout 90 inch/pounds (612 cm/kg) and the prevailing off torque is about200 inch/pounds (1360 cm/kg).

EXAMPLE 3

Another suitable anaerobically-curing composition in accordance with thepresent invention is prepared using the following ingredients combinedin the order indicated:

    ______________________________________                                                          Parts by Weight                                             ______________________________________                                        Tetraethyleneglycol 100                                                       dimethacrylate                                                                2,4-Bis-(trichloromethyl)-6-                                                                      3                                                         methyl-s-triazine                                                             Trifluoromethanesulfonanilide                                                                     3                                                         Methylhydroquinone  0.01                                                      ______________________________________                                    

The above composition exhibits a suitable shelf-life when stored in thepresence of oxygen and cures rapidly when applied to an active metalsurface once oxygen is excluded.

EXAMPLE 4

In illustrating another halogen-containing compound which can besuitably employed in the anaerobically-curing compositions of thepresent invention, a composition is prepared using the followingingredients which are combined in the order indicated.

    ______________________________________                                                          Parts by Weight                                             ______________________________________                                        Tetraethyleneglycol 100                                                       dimethacrylate                                                                2,4,6-Tris-(tribromomethyl)-s-                                                                    2                                                         triazine                                                                      N,N--dimethyl-p-toluidine                                                                         2                                                         Methylhydroquinone  0.01                                                      ______________________________________                                    

The above composition exhibits a suitable shelf-life when stored in thepresence of oxygen and cures rapidly when applied to an active metalsurface once oxygen is excluded.

When the above composition is tested in accordance with Test Method B,the handling time is less than about 2 hours and the overlap shear is200 pounds per square inch (14.1 kg/cm²).

EXAMPLE 5

In illustrating yet another halogen-containing compound which can besuitably employed in the anaerobically-curing composition of the presentinvention, a composition is prepared using the following ingredientswhich are combined in the order indicated:

    ______________________________________                                                         Parts by Weight                                              ______________________________________                                        Tetraethyleneglycol                                                                              100                                                        dimethacrylate                                                                2,4-bis(trichloromethyl)-6-p-                                                                    2                                                          methoxystyryl-s-triazine                                                      (described in U.S. Pat. No.                                                   3,987,037 (Bonham et al.))                                                    N,N--dimethyl-p-toluidine                                                                        2                                                          Methylhydroquinione                                                                              0.01                                                       ______________________________________                                    

The above composition exhibits a suitable shelf-life when stored in thepresence of oxygen and cures rapidly when applied to an active metalsurface once oxygen is excluded.

When the above composition is tested in accordance with Test Method B,the handling time is less than about 2 hours and the handling time isless than about 2 hours and the overlap shear value is 200 pounds persquare inch (14.1 kgcm²).

EXAMPLE 6

In illustrating yet another halogen-containing compound which can besuitably employed in the anaerobically-curing composition of the presentinvention, a composition is prepared using the following ingredientswhich are combined in the order indicated:

    ______________________________________                                                          Parts by Weight                                             ______________________________________                                        Tetraethyleneglycol 100                                                       dimethacrylate                                                                2,4-Bis-(trichloromethyl)-6-                                                                      2                                                         methyl-s-triazine                                                             Homopiperidine (available from                                                                    2                                                         Aldrich Chemical)                                                             Methylhydroquinone  0.01                                                      ______________________________________                                    

The above composition exhibits a suitable shelf-life when stored in thepresence of oxygen and cures rapidly when applied to an active metalsurface once oxygen is excluded.

When the above composition is tested in accordance with Test Method B,the handling time is less than about 2 hours.

EXAMPLE 7

In illustrating yet another halogen-containing compound which can besuitably employed in the anaerobically-curing composition of the presentinvention, a composition is prepared using the following ingredientswhich are combined in the order indicated:

    ______________________________________                                                           Parts by Weight                                            ______________________________________                                        Tetraethyleneglycol dimethacrylate                                                                 100                                                      α,α,α-Trichlorotoluene                                                           2                                                        N,N--dimethyl-p-toluidine                                                                          2                                                        Methylhydroquinone   0.01                                                     ______________________________________                                    

The above composition exhibits a suitable shelf-life when stored in thepresence of oxygen and cures rapidly when applied to an active metalsurface once oxygen is excluded.

When the above composition is tested in accordance with Test method B,the handling time is less than about 2 hours and the overlap shear valueis about 180 pounds per square inch (12.7 kg/cm²).

EXAMPLE 8

In illustrating yet another halogen-containing compound which can besuitably employed in the anaerobically-curing compositions of thepresent invention, a composition is prepared using the followingingredients which are combined in the order indicated:

    ______________________________________                                                           Parts by Weight                                            ______________________________________                                        Tetraethyleneglycol dimethacrylate                                                                 100                                                      Dibromocyanoacetamide                                                                              2                                                        N,N--dimethyl-p-toluidine                                                                          2                                                        Methylhydroquinone   0.01                                                     ______________________________________                                    

The above composition exhibits a suitable shelf-life when stored in thepresence of oxygen and cures rapidly when applied to an active metalsurface once oxygen is excluded.

When the above composition is tested in accordance with Test Method B,the handling time is less than about 2 hours and the overlap shear valueis about 200 pounds per square inch (14.1 kg/cm²).

EXAMPLE 9

A suitable anaearobically-curing composition which is in accordance withthe present invention and which comprises a pressure-sensitive polymeris prepared from the following ingredients:

    ______________________________________                                                          Parts by Weight                                             ______________________________________                                        Isobutyl acrylate (90% by                                                                         7.0                                                       weight)/acrylic acid (10% by                                                  weight) copolymer (prepared                                                   in accordance with the                                                        procedures of in U.S. Pat.                                                    No. Re. 24,906 (Ulrich),                                                      incorporated herein by reference)                                             "Epocryl 12" (a reaction product                                                                  2                                                         of methacrylic acid and an                                                    epoxy resin; available from                                                   Shell Chemical Co.)                                                           Methacrylic acid    2                                                         2,4-Bis-(trichloromethyl)-6-                                                                      0.3                                                       methyl-s-triazine                                                             Homopiperidine      0.3                                                       Benzoquinone        0.005                                                     Methyl ethyl ketone 7.6                                                       ______________________________________                                    

When the above composition is tested in accordance with Test Method Bexcept that here a jaw separation rate of 1 inch (2.54 cm) per minute isemployed and the aluminum strips are unetched and have been wiped withmethyl ethyl ketone prior to priming, the overlap shear value is about1000 pounds per square inch (70.3 kg/cm²).

EXAMPLE 10

Another suitable anaerobically-curing composition which is in accordancewith the present invention and which comprises a pressure-sensitivepolymer is prepared from the following ingredients:

    ______________________________________                                                            Parts by Weight                                           ______________________________________                                        Isobutyl acrylate (85)/n-butylacrylate                                                              14.4                                                    (10)/acrylic acid (5) terpolymer                                              (prepared in accordance with the                                              procedures of said U.S. Pat. No.                                              Re. 24,906)                                                                   Tetraethylene glycol dimethacrylate                                                                 3.0                                                     Methacrylic acid      3.0                                                     α,α,α,α',α',α',-hexachloro-p-xylene                             0.3                                                     Saccharin             0.8                                                     Methyl hydroquinone   0.043                                                   Methyl ethyl ketone   46.6                                                    ______________________________________                                    

In testing the performance of this composition, 4"×6"(10cm ×15.2 cm)aluminum panels were primed with a 3% (weight to weight) solution of"Vanax 808" (condensation reaction product of butylaldehyde and aniline,commercially available from R. T. Vanderbilt Chemical Company). Afterthe solvent evaporated, a 8-mil (0.2 mm) coating of the above adhesivecomposition was applied to one of the primed aluminum panels. After 30minutes the second primed aluminum panel was placed over the first togive a one square inch area of adhesive bonding. The bond was allowed tocondition 24 hours at room temperature, at which time one inch strips ofthe laminate were cut. The overlap shear valve was then determined to beabout 800 pounds per square using an Instron Dynamic Tester operated at0.2 inch (0.51 cm) per minute.

I claim:
 1. An anaerobically-curing composition, comprising(A) apolymerizable monomer having at least one α,β-saturated carboxylfunctionality per molecule of monomer; (B) an effective amount ofhalogen-containing compound as a first initiator component and selectedfrom the group consisting of halogenated triazines of the formula##STR14## wherein: X³ and X⁴ are each selected independently from thegroup consisting of H, CH₃, Cl, and Br; Y³, Y⁴, Z³ and Z⁴ are eachindependently selected from the group consisting of Cl and Br; and R³ isselected from the group consisting of H and organic radicals comprising1 to about 10 carbons; and compounds of the formula ##STR15## wherein:X² is selected from the group consisting of H, Cl, Br and CN; Y² and Z²are each selected independently from the group consisting of Cl and Br;R² is selected from the group consisting of amino residues and organicradicals comprising 1 to about 10 carbons;p is 0 or 1; q is 0 or 1; andr is 1 or 2; (C) an effective amount of second initiator componentselected from organic sulfimides, perfluoroalkyl sulfonanilides,secondary amines of the formula ##STR16## wherein: R⁴ and R⁵ are eachhydrocarbon groups comprising 1 to about 12 carbons; tertiary amines ofthe formula ##STR17## wherein: R⁶, R⁷ and R⁸ are in each hydrocarbongroups comprising 1 to about 12 carbons; and tertiary amines of theformula ##STR18## wherein: R⁹ and R¹⁰ are each hydrocarbon groupscomprising up to about 12 carbons; A is a carbocyclic aromatic nucleusselected from the group consisting of phenyl and naphthyl radicals; R¹¹is an organic radical group comprising up to about 5 carbons and isselected from the group consisting of alkyl and alkoxy radicals; and tis from 0 to 3 inclusive; (D) a sufficient amount of an inhibitor offree-radical polymerization to retard polymerization of said adhesivecomposition while in the presence of air;said composition being capableof polymerizing when placed in an anaerobically-curable environment. 2.An anaerobically-curing composition in accordance with claim 1, whereinsaid monomer is present in an amount of 100 parts by weight, said firstinitiator component is present in an amount of about 0.5 to 20 parts byweight, and said second initiator component is present in an amount ofabout 0.5 to 20 parts by weight.
 3. An anaerobically-curing compositionin accordance with claim 2, wherein said monomer is selected from thegroup consisting of triethyleneglycol dimethacrylate, ethyleneglycoldimethacrylate, tetraethyleneglycol dimethacrylate, polyethyleneglycoldimethacrylate, polyethylene glycol diacrylate, 1,3-butyleneglycoldimethacrylate, trimethylol propane trimethacrylate, neopentylglycoldimethacrylate, ethoxylated bisphenol A dimethacrylate, propoxylatedbisphenol C dimethacrylate, bisphenol A bis(2-hydroxypropyl)dimethacrylate, cyclohexyl methacrylate, 2-ethylhexyl methacrylate,hydroxyethyl methacrylate, isooctyl acrylate, n-butyl acrylate,methacrylic acid, the 2-hydroxyethyl methacrylate half-ester of maleicacid, and monomeric polyacrylate esters formed from isocyanates.
 4. Ananaerobically-curing composition in accordance with claim 2, whereinsaid first initiator component is said halogenated triazine.
 5. Acomposition in accordance with claim 4, wherein said halogen-containingcompound is selected from the group consisting of2,4-bis-(trichloromethyl)-6-methyl-s-triazine,2,4,6-tris-(trichloromethyl)-s-triazine,2,4,6-tris-(tribromomethyl)-s-triazine,2,4-bis-(trichloromethyl)-6-p-methoxystyryl-s-triazine and ##STR19## 6.An anaerobically-curing composition in accordance with claim 4, whereinsaid second initiator component is an organic sulfimide of the formula##STR20## wherein: R¹² and R¹³ are organic radicals comprising up toabout 10 carbons.
 7. An anaerobically-curing composition in accordancewith claim 4, wherein said second initiator component is aperfluoroalkyl sulfonanilide.
 8. An anaerobically-curing composition inaccordance with claim 4, wherein said second initiator component is atertiary amine selected from the group consisting ofN,N-diethyl-p-toluidine, N,N-dimethylaniline, N,N-diethylaniline, andN,N-dimethyl-p-toluidine.
 9. An anaerobically-curing composition inaccordance with claim 4, wherein said first initiator component ispresent in an amount of 1 to 10 parts by weight and said secondinitiator component is present in an amount of 1 to 10 parts by weight.10. An anaerobically-curing composition in accordance with claim 1,wherein said inhibitor is a quinone-type inhibitor which is present inan amount of about 0.001 to 0.03 parts by weight.
 11. Ananaerobically-curing composition comprising:(A) a polymerizable monomerhaving at least one α,β-saturated carboxyl functionality per molecule ofmonomer; (B) an effective amount of halogen-containing compound as afirst initiator component and selected from compounds of the formula##STR21## wherein: x¹ is selected from the group consisting of H, CH₃,Cl and Br; Y¹ and Z¹ are each selected independently from the groupconsisting of Cl and Br; R¹ is selected from the group consisting ofaromatic and heteroaromatic residues; and n is an integer from 1 to 3inclusive; (C) an effective amount of a second initiator componentselected from compounds of the group consisting of organic sulfimidesand perfluoroalkyl sulfonanilides; (D) a sufficient amount of aninhibitor of free-radical polymerization to retard polymerization ofsaid composition while in the presence of air;said composition beingcapable of polymerizing when placed in an anaerobically-curableenvironment.
 12. An anaerobically-curing composition in accordance withclaim 11, wherein said monomer is present in an amount of 100 parts byweight, said first initiator component is present in an amount of about0.5 to 20 parts by weight, and said second initiator component ispresent in an amount of about 0.5 to 20 parts by weight.
 13. Ananaerobically-curing composition in accordance with claim 11, whereinsaid second initiator component is an organic sulfimide of the formula##STR22## wherein: R12 and R13 are organic radicals comprising up toabout 10 carbons.
 14. An anaerobically-curing composition in accordancewith claim 11, wherein said second initiator component is aperfluoroalkyl sulfonanilide.